SAE-AISI H10 Steel vs. C86500 Bronze

SAE-AISI H10 steel belongs to the iron alloys classification, while C86500 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H10 steel and the bottom bar is C86500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 74
40
Tensile Strength: Ultimate (UTS), MPa 680 to 2030
530

Thermal Properties

Latent Heat of Fusion, J/g 270
170
Melting Completion (Liquidus), °C 1470
880
Melting Onset (Solidus), °C 1420
860
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 38
86
Thermal Expansion, µm/m-K 12
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
22
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
25

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
23
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.4
2.8
Embodied Energy, MJ/kg 48
48
Embodied Water, L/kg 71
330

Common Calculations

Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 24 to 72
19
Strength to Weight: Bending, points 22 to 46
18
Thermal Diffusivity, mm2/s 10
28
Thermal Shock Resistance, points 22 to 66
17

Alloy Composition

Aluminum (Al), % 0
0.5 to 1.5
Carbon (C), % 0.35 to 0.45
0
Chromium (Cr), % 3.0 to 3.8
0
Copper (Cu), % 0 to 0.25
55 to 60
Iron (Fe), % 89.5 to 93.4
0.4 to 2.0
Lead (Pb), % 0
0 to 0.4
Manganese (Mn), % 0.25 to 0.7
0.1 to 1.5
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 0 to 0.3
0 to 1.0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.8 to 1.2
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 1.0
Vanadium (V), % 0.25 to 0.75
0
Zinc (Zn), % 0
36 to 42
Residuals, % 0
0 to 1.0