SAE-AISI H11 Steel vs. CC750S Brass

SAE-AISI H11 steel belongs to the iron alloys classification, while CC750S brass belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H11 steel and the bottom bar is CC750S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 74
40
Tensile Strength: Ultimate (UTS), MPa 690 to 1840
200

Thermal Properties

Latent Heat of Fusion, J/g 270
170
Melting Completion (Liquidus), °C 1460
860
Melting Onset (Solidus), °C 1410
810
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 42
110
Thermal Expansion, µm/m-K 12
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.2
24
Electrical Conductivity: Equal Weight (Specific), % IACS 9.5
26

Otherwise Unclassified Properties

Base Metal Price, % relative 5.5
25
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 3.0
2.8
Embodied Energy, MJ/kg 43
46
Embodied Water, L/kg 75
330

Common Calculations

Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 25 to 66
6.8
Strength to Weight: Bending, points 22 to 43
9.3
Thermal Diffusivity, mm2/s 11
35
Thermal Shock Resistance, points 22 to 58
6.7

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.33 to 0.43
0
Chromium (Cr), % 4.8 to 5.5
0
Copper (Cu), % 0 to 0.25
62 to 67
Iron (Fe), % 89.6 to 92.5
0 to 0.8
Lead (Pb), % 0
1.0 to 3.0
Manganese (Mn), % 0.2 to 0.5
0 to 0.2
Molybdenum (Mo), % 1.1 to 1.6
0
Nickel (Ni), % 0 to 0.3
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.050
Silicon (Si), % 0.8 to 1.2
0 to 0.050
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 1.5
Vanadium (V), % 0.3 to 0.6
0
Zinc (Zn), % 0
26.3 to 36