SAE-AISI H11 Steel vs. SAE-AISI H24 Steel

Both SAE-AISI H11 steel and SAE-AISI H24 steel are iron alloys. They have 85% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H11 steel and the bottom bar is SAE-AISI H24 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 690 to 1840
720 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 270
240
Melting Completion (Liquidus), °C 1460
1750
Melting Onset (Solidus), °C 1410
1700
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 42
27
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 5.5
37
Density, g/cm3 7.8
9.1
Embodied Carbon, kg CO2/kg material 3.0
6.1
Embodied Energy, MJ/kg 43
93
Embodied Water, L/kg 75
78

Common Calculations

PREN (Pitting Resistance) 9.6
28
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 25 to 66
22 to 61
Strength to Weight: Bending, points 22 to 43
20 to 39
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 22 to 58
22 to 61

Alloy Composition

Carbon (C), % 0.33 to 0.43
0.42 to 0.53
Chromium (Cr), % 4.8 to 5.5
2.5 to 3.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 89.6 to 92.5
78 to 82.4
Manganese (Mn), % 0.2 to 0.5
0.15 to 0.4
Molybdenum (Mo), % 1.1 to 1.6
0
Nickel (Ni), % 0 to 0.3
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.8 to 1.2
0.15 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
14 to 16
Vanadium (V), % 0.3 to 0.6
0.4 to 0.6

Comparable Variants