SAE-AISI H13 Steel vs. 4007 Aluminum

SAE-AISI H13 steel belongs to the iron alloys classification, while 4007 aluminum belongs to the aluminum alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is 4007 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
71
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 74
27
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
130 to 160

Thermal Properties

Latent Heat of Fusion, J/g 270
410
Melting Completion (Liquidus), °C 1460
650
Melting Onset (Solidus), °C 1420
590
Specific Heat Capacity, J/kg-K 470
890
Thermal Conductivity, W/m-K 29
170
Thermal Expansion, µm/m-K 10
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.3
42
Electrical Conductivity: Equal Weight (Specific), % IACS 9.7
140

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
9.5
Density, g/cm3 7.8
2.8
Embodied Carbon, kg CO2/kg material 4.3
8.1
Embodied Energy, MJ/kg 64
150
Embodied Water, L/kg 78
1160

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
49
Strength to Weight: Axial, points 25 to 65
12 to 15
Strength to Weight: Bending, points 22 to 43
20 to 23
Thermal Diffusivity, mm2/s 7.8
67
Thermal Shock Resistance, points 25 to 65
5.5 to 6.7

Alloy Composition

Aluminum (Al), % 0
94.1 to 97.6
Carbon (C), % 0.32 to 0.45
0
Chromium (Cr), % 4.8 to 5.5
0.050 to 0.25
Cobalt (Co), % 0
0 to 0.050
Copper (Cu), % 0 to 0.25
0 to 0.2
Iron (Fe), % 88.8 to 92
0.4 to 1.0
Magnesium (Mg), % 0
0 to 0.2
Manganese (Mn), % 0.2 to 0.5
0.8 to 1.5
Molybdenum (Mo), % 1.1 to 1.8
0
Nickel (Ni), % 0 to 0.3
0.15 to 0.7
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.8 to 1.2
1.0 to 1.7
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0.8 to 1.2
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15

Comparable Variants