SAE-AISI H13 Steel vs. EN 1.5507 Steel
Both SAE-AISI H13 steel and EN 1.5507 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is EN 1.5507 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 1820 | |
| 450 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 29 | |
| 49 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.3 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.0 | |
| 2.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 1.4 |
| Embodied Energy, MJ/kg | 64 | |
| 19 |
| Embodied Water, L/kg | 78 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 25 to 65 | |
| 16 to 31 |
| Strength to Weight: Bending, points | 22 to 43 | |
| 17 to 26 |
| Thermal Diffusivity, mm2/s | 7.8 | |
| 13 |
| Thermal Shock Resistance, points | 25 to 65 | |
| 13 to 26 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.080 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.32 to 0.45 | |
| 0.21 to 0.25 |
| Chromium (Cr), % | 4.8 to 5.5 | |
| 0.25 to 0.35 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 88.8 to 92 | |
| 97.8 to 98.7 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0.8 to 1.0 |
| Molybdenum (Mo), % | 1.1 to 1.8 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.8 to 1.2 | |
| 0 to 0.15 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.060 |
| Vanadium (V), % | 0.8 to 1.2 | |
| 0 |