SAE-AISI H13 Steel vs. R60901 Alloy

SAE-AISI H13 steel belongs to the iron alloys classification, while R60901 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H13 steel and the bottom bar is R60901 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
98
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
37
Tensile Strength: Ultimate (UTS), MPa 690 to 1820
500 to 580

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 29
17
Thermal Expansion, µm/m-K 10
6.3

Otherwise Unclassified Properties

Density, g/cm3 7.8
6.6
Embodied Water, L/kg 78
270

Common Calculations

Stiffness to Weight: Axial, points 14
8.3
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 25 to 65
21 to 25
Strength to Weight: Bending, points 22 to 43
21 to 24
Thermal Diffusivity, mm2/s 7.8
9.7
Thermal Shock Resistance, points 25 to 65
58 to 67

Alloy Composition

Carbon (C), % 0.32 to 0.45
0
Chromium (Cr), % 4.8 to 5.5
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 88.8 to 92
0
Manganese (Mn), % 0.2 to 0.5
0
Molybdenum (Mo), % 1.1 to 1.8
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0
2.4 to 2.8
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.8 to 1.2
0
Sulfur (S), % 0 to 0.030
0
Vanadium (V), % 0.8 to 1.2
0
Zirconium (Zr), % 0
96.8 to 97.5
Residuals, % 0
0 to 0.29