SAE-AISI H14 Steel vs. 85-platinum 15-iridium
SAE-AISI H14 steel belongs to the iron alloys classification, while 85-platinum 15-iridium belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is SAE-AISI H14 steel and the bottom bar is 85-platinum 15-iridium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Poisson's Ratio | 0.29 | |
| 0.38 |
| Shear Modulus, GPa | 75 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 2030 | |
| 560 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 110 |
| Melting Completion (Liquidus), °C | 1530 | |
| 1820 |
| Melting Onset (Solidus), °C | 1490 | |
| 1790 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 8.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.3 | |
| 6.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 2.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 22 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 5.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 9.3 |
| Strength to Weight: Axial, points | 24 to 69 | |
| 7.1 to 9.3 |
| Strength to Weight: Bending, points | 22 to 44 | |
| 6.9 to 8.3 |
| Thermal Shock Resistance, points | 24 to 68 | |
| 21 to 28 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.45 | |
| 0 |
| Chromium (Cr), % | 4.8 to 5.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iridium (Ir), % | 0 | |
| 14.5 to 15.5 |
| Iron (Fe), % | 86.5 to 89.9 | |
| 0 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 84.3 to 85.5 |
| Silicon (Si), % | 0.8 to 1.2 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 4.0 to 5.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |