SAE-AISI H14 Steel vs. ASTM A732 Cast Steel

Both SAE-AISI H14 steel and ASTM A732 cast steel are iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H14 steel and the bottom bar is ASTM A732 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
72 to 73
Tensile Strength: Ultimate (UTS), MPa 710 to 2030
460 to 1470

Thermal Properties

Latent Heat of Fusion, J/g 270
250 to 260
Melting Completion (Liquidus), °C 1530
1440 to 1460
Melting Onset (Solidus), °C 1490
1400 to 1420
Specific Heat Capacity, J/kg-K 460
470 to 480
Thermal Conductivity, W/m-K 35
39 to 50
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
7.1 to 7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.2 to 8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.0 to 3.8
Density, g/cm3 8.1
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 2.7
1.4 to 1.7
Embodied Energy, MJ/kg 39
19 to 24
Embodied Water, L/kg 73
47 to 54

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 69
16 to 52
Strength to Weight: Bending, points 22 to 44
17 to 37
Thermal Diffusivity, mm2/s 9.3
10 to 14
Thermal Shock Resistance, points 24 to 68
14 to 43