SAE-AISI H14 Steel vs. N08221 Nickel

SAE-AISI H14 steel belongs to the iron alloys classification, while N08221 nickel belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H14 steel and the bottom bar is N08221 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 710 to 2030
610

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Melting Completion (Liquidus), °C 1530
1440
Melting Onset (Solidus), °C 1490
1390
Specific Heat Capacity, J/kg-K 460
460
Thermal Expansion, µm/m-K 11
13

Otherwise Unclassified Properties

Base Metal Price, % relative 15
44
Density, g/cm3 8.1
8.3
Embodied Carbon, kg CO2/kg material 2.7
7.9
Embodied Energy, MJ/kg 39
110
Embodied Water, L/kg 73
240

Common Calculations

PREN (Pitting Resistance) 13
40
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 69
21
Strength to Weight: Bending, points 22 to 44
19
Thermal Shock Resistance, points 24 to 68
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.2
Carbon (C), % 0.35 to 0.45
0 to 0.025
Chromium (Cr), % 4.8 to 5.5
20 to 22
Copper (Cu), % 0 to 0.25
1.5 to 3.0
Iron (Fe), % 86.5 to 89.9
22 to 33.9
Manganese (Mn), % 0.2 to 0.5
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 6.5
Nickel (Ni), % 0 to 0.3
39 to 46
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.8 to 1.2
0 to 0.050
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0.6 to 1.0
Tungsten (W), % 4.0 to 5.3
0