SAE-AISI H14 steel belongs to the iron alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 12 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H14 steel and the bottom bar is Z21210 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Tensile Strength: Ultimate (UTS), MPa 710 to 2030
150 to 170

Thermal Properties

Melting Completion (Liquidus), °C 1530
420
Melting Onset (Solidus), °C 1490
420
Specific Heat Capacity, J/kg-K 460
400
Thermal Conductivity, W/m-K 35
110
Thermal Expansion, µm/m-K 11
32

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
28
Electrical Conductivity: Equal Weight (Specific), % IACS 10
35

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.1

Common Calculations

Strength to Weight: Axial, points 24 to 69
5.7 to 6.4
Strength to Weight: Bending, points 22 to 44
8.6 to 9.4
Thermal Diffusivity, mm2/s 9.3
38