SAE-AISI H21 Steel vs. SAE-AISI M42 Steel
Both SAE-AISI H21 steel and SAE-AISI M42 steel are iron alloys. They have 85% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI H21 steel and the bottom bar is SAE-AISI M42 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 1790 | |
| 810 to 2310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Melting Completion (Liquidus), °C | 1630 | |
| 1540 |
| Melting Onset (Solidus), °C | 1580 | |
| 1490 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 27 | |
| 20 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 30 |
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 7.4 |
| Embodied Energy, MJ/kg | 68 | |
| 100 |
| Embodied Water, L/kg | 72 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 38 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 58 | |
| 28 to 79 |
| Strength to Weight: Bending, points | 21 to 38 | |
| 24 to 48 |
| Thermal Diffusivity, mm2/s | 7.1 | |
| 5.4 |
| Thermal Shock Resistance, points | 24 to 59 | |
| 25 to 71 |
Alloy Composition
| Carbon (C), % | 0.28 to 0.36 | |
| 1.1 to 1.2 |
| Chromium (Cr), % | 3.0 to 3.8 | |
| 3.5 to 4.3 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 87.6 to 93.8 | |
| 76.3 to 81 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 10 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.5 | |
| 0.15 to 0.65 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 8.5 to 10 | |
| 1.2 to 1.9 |
| Vanadium (V), % | 0.3 to 0.6 | |
| 1.0 to 1.4 |