SAE-AISI H21 Steel vs. C51900 Bronze
SAE-AISI H21 steel belongs to the iron alloys classification, while C51900 bronze belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H21 steel and the bottom bar is C51900 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 1790 | |
| 380 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 200 |
| Melting Completion (Liquidus), °C | 1630 | |
| 1040 |
| Melting Onset (Solidus), °C | 1580 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 380 |
| Thermal Conductivity, W/m-K | 27 | |
| 66 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 33 |
| Density, g/cm3 | 8.5 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 4.5 | |
| 3.2 |
| Embodied Energy, MJ/kg | 68 | |
| 51 |
| Embodied Water, L/kg | 72 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 23 to 58 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 21 to 38 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 7.1 | |
| 20 |
| Thermal Shock Resistance, points | 24 to 59 | |
| 14 to 22 |
Alloy Composition
| Carbon (C), % | 0.28 to 0.36 | |
| 0 |
| Chromium (Cr), % | 3.0 to 3.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 91.7 to 95 |
| Iron (Fe), % | 87.6 to 93.8 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.030 to 0.35 |
| Silicon (Si), % | 0.15 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 5.0 to 7.0 |
| Tungsten (W), % | 8.5 to 10 | |
| 0 |
| Vanadium (V), % | 0.3 to 0.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |