SAE-AISI H22 Steel vs. AWS E33-31
Both SAE-AISI H22 steel and AWS E33-31 are iron alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H22 steel and the bottom bar is AWS E33-31.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1920 | |
| 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1380 |
| Melting Onset (Solidus), °C | 1620 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 36 |
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 6.0 |
| Embodied Energy, MJ/kg | 73 | |
| 86 |
| Embodied Water, L/kg | 72 | |
| 260 |
Common Calculations
| PREN (Pitting Resistance) | 21 | |
| 44 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 61 | |
| 28 |
| Strength to Weight: Bending, points | 20 to 39 | |
| 24 |
| Thermal Shock Resistance, points | 22 to 60 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.3 to 0.4 | |
| 0 to 0.030 |
| Chromium (Cr), % | 1.8 to 3.8 | |
| 31 to 35 |
| Copper (Cu), % | 0 to 0.25 | |
| 0.4 to 0.8 |
| Iron (Fe), % | 82.2 to 87.4 | |
| 24.7 to 34.8 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 2.5 to 4.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 30 to 32 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0 to 0.9 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Tungsten (W), % | 10 to 11.8 | |
| 0 |
| Vanadium (V), % | 0.25 to 0.5 | |
| 0 |