SAE-AISI H22 Steel vs. EN 1.5682 Steel
Both SAE-AISI H22 steel and EN 1.5682 steel are iron alloys. They have 86% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H22 steel and the bottom bar is EN 1.5682 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 1920 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1450 |
| Melting Onset (Solidus), °C | 1620 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 7.5 |
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.9 | |
| 2.3 |
| Embodied Energy, MJ/kg | 73 | |
| 31 |
| Embodied Water, L/kg | 72 | |
| 63 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 61 | |
| 27 |
| Strength to Weight: Bending, points | 20 to 39 | |
| 23 |
| Thermal Shock Resistance, points | 22 to 60 | |
| 23 |
Alloy Composition
| Carbon (C), % | 0.3 to 0.4 | |
| 0 to 0.13 |
| Chromium (Cr), % | 1.8 to 3.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.3 |
| Iron (Fe), % | 82.2 to 87.4 | |
| 88.7 to 91.1 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.3 | |
| 8.5 to 9.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0050 |
| Tungsten (W), % | 10 to 11.8 | |
| 0 |
| Vanadium (V), % | 0.25 to 0.5 | |
| 0 to 0.050 |