SAE-AISI H22 Steel vs. SAE-AISI H19 Steel

Both SAE-AISI H22 steel and SAE-AISI H19 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI H22 steel and the bottom bar is SAE-AISI H19 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 700 to 1920
720 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1670
1540
Melting Onset (Solidus), °C 1620
1490
Specific Heat Capacity, J/kg-K 440
460
Thermal Conductivity, W/m-K 31
29
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 28
22
Density, g/cm3 8.7
8.2
Embodied Carbon, kg CO2/kg material 4.9
7.5
Embodied Energy, MJ/kg 73
110
Embodied Water, L/kg 72
110

Common Calculations

PREN (Pitting Resistance) 21
13
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
24
Strength to Weight: Axial, points 22 to 61
24 to 68
Strength to Weight: Bending, points 20 to 39
22 to 43
Thermal Diffusivity, mm2/s 8.2
7.9
Thermal Shock Resistance, points 22 to 60
21 to 59

Alloy Composition

Carbon (C), % 0.3 to 0.4
0.32 to 0.45
Chromium (Cr), % 1.8 to 3.8
4.0 to 4.8
Cobalt (Co), % 0
4.0 to 4.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 82.2 to 87.4
81.4 to 85.5
Manganese (Mn), % 0.15 to 0.4
0.2 to 0.5
Molybdenum (Mo), % 0
0.3 to 0.55
Nickel (Ni), % 0 to 0.3
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.15 to 0.4
0.2 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 10 to 11.8
3.8 to 4.5
Vanadium (V), % 0.25 to 0.5
1.8 to 2.2

Comparable Variants