SAE-AISI H23 Steel vs. SAE-AISI M1 Steel
Both SAE-AISI H23 steel and SAE-AISI M1 steel are iron alloys. They have 82% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI H23 steel and the bottom bar is SAE-AISI M1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1550 | |
| 730 to 2140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Melting Completion (Liquidus), °C | 1680 | |
| 1560 |
| Melting Onset (Solidus), °C | 1630 | |
| 1510 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 20 | |
| 29 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 18 |
| Density, g/cm3 | 8.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 6.9 | |
| 7.0 |
| Embodied Energy, MJ/kg | 110 | |
| 99 |
| Embodied Water, L/kg | 120 | |
| 98 |
Common Calculations
| PREN (Pitting Resistance) | 32 | |
| 35 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 49 | |
| 25 to 73 |
| Strength to Weight: Bending, points | 21 to 34 | |
| 22 to 45 |
| Thermal Diffusivity, mm2/s | 5.2 | |
| 8.0 |
| Thermal Shock Resistance, points | 23 to 47 | |
| 23 to 66 |
Alloy Composition
| Carbon (C), % | 0.25 to 0.35 | |
| 0.78 to 0.88 |
| Chromium (Cr), % | 11 to 12.8 | |
| 3.5 to 4.0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 71.3 to 76.7 | |
| 81 to 84.8 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 8.2 to 9.2 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.6 | |
| 0.2 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 11 to 12.8 | |
| 1.4 to 2.1 |
| Vanadium (V), % | 0.75 to 1.3 | |
| 1.0 to 1.4 |