SAE-AISI H23 Steel vs. R05400 Tantalum
SAE-AISI H23 steel belongs to the iron alloys classification, while R05400 tantalum belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H23 steel and the bottom bar is R05400 tantalum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 80 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 760 to 1550 | |
| 210 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 140 |
| Thermal Conductivity, W/m-K | 20 | |
| 59 |
| Thermal Expansion, µm/m-K | 12 | |
| 6.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 17 |
| Embodied Water, L/kg | 120 | |
| 650 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 6.2 |
| Stiffness to Weight: Bending, points | 22 | |
| 11 |
| Strength to Weight: Axial, points | 24 to 49 | |
| 3.6 to 9.0 |
| Strength to Weight: Bending, points | 21 to 34 | |
| 4.8 to 8.8 |
| Thermal Diffusivity, mm2/s | 5.2 | |
| 25 |
| Thermal Shock Resistance, points | 23 to 47 | |
| 13 to 32 |
Alloy Composition
| Carbon (C), % | 0.25 to 0.35 | |
| 0 to 0.010 |
| Chromium (Cr), % | 11 to 12.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 71.3 to 76.7 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.030 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.6 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 99.7 to 100 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 11 to 12.8 | |
| 0 to 0.050 |
| Vanadium (V), % | 0.75 to 1.3 | |
| 0 |