SAE-AISI H26 Steel vs. SAE-AISI M33 Steel
Both SAE-AISI H26 steel and SAE-AISI M33 steel are iron alloys. They have 82% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI H26 steel and the bottom bar is SAE-AISI M33 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 2100 | |
| 810 to 2210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 270 |
| Melting Completion (Liquidus), °C | 1810 | |
| 1550 |
| Melting Onset (Solidus), °C | 1760 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Conductivity, W/m-K | 22 | |
| 20 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 32 |
| Density, g/cm3 | 9.3 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 7.7 |
| Embodied Energy, MJ/kg | 120 | |
| 110 |
| Embodied Water, L/kg | 90 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 34 | |
| 38 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 63 | |
| 27 to 75 |
| Strength to Weight: Bending, points | 19 to 39 | |
| 24 to 46 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 5.5 |
| Thermal Shock Resistance, points | 22 to 63 | |
| 25 to 68 |
Alloy Composition
| Carbon (C), % | 0.45 to 0.55 | |
| 0.85 to 0.92 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 3.5 to 4.0 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 73.3 to 77.5 | |
| 71.4 to 76.3 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 10 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0.15 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 17.3 to 19 | |
| 1.3 to 2.1 |
| Vanadium (V), % | 0.75 to 1.3 | |
| 1.0 to 1.4 |