SAE-AISI H26 Steel vs. C17300 Copper
SAE-AISI H26 steel belongs to the iron alloys classification, while C17300 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI H26 steel and the bottom bar is C17300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 80 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 2100 | |
| 500 to 1380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 230 |
| Melting Completion (Liquidus), °C | 1810 | |
| 980 |
| Melting Onset (Solidus), °C | 1760 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 380 |
| Thermal Conductivity, W/m-K | 22 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 9.4 |
| Embodied Energy, MJ/kg | 120 | |
| 150 |
| Embodied Water, L/kg | 90 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 21 | |
| 19 |
| Strength to Weight: Axial, points | 22 to 63 | |
| 16 to 44 |
| Strength to Weight: Bending, points | 19 to 39 | |
| 16 to 31 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 32 |
| Thermal Shock Resistance, points | 22 to 63 | |
| 17 to 48 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 1.8 to 2.0 |
| Carbon (C), % | 0.45 to 0.55 | |
| 0 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 95.5 to 97.8 |
| Iron (Fe), % | 73.3 to 77.5 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 | |
| 0.2 to 0.6 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0.2 to 0.6 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.4 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 17.3 to 19 | |
| 0 |
| Vanadium (V), % | 0.75 to 1.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |