SAE-AISI H26 Steel vs. C83400 Brass

SAE-AISI H26 steel belongs to the iron alloys classification, while C83400 brass belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H26 steel and the bottom bar is C83400 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
110
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 80
42
Tensile Strength: Ultimate (UTS), MPa 720 to 2100
240

Thermal Properties

Latent Heat of Fusion, J/g 240
200
Melting Completion (Liquidus), °C 1810
1040
Melting Onset (Solidus), °C 1760
1020
Specific Heat Capacity, J/kg-K 410
380
Thermal Conductivity, W/m-K 22
190
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 45
29
Density, g/cm3 9.3
8.7
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 120
43
Embodied Water, L/kg 90
320

Common Calculations

Stiffness to Weight: Axial, points 12
7.2
Stiffness to Weight: Bending, points 21
19
Strength to Weight: Axial, points 22 to 63
7.7
Strength to Weight: Bending, points 19 to 39
9.9
Thermal Diffusivity, mm2/s 5.6
57
Thermal Shock Resistance, points 22 to 63
8.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0.45 to 0.55
0
Chromium (Cr), % 3.8 to 4.5
0
Copper (Cu), % 0 to 0.25
88 to 92
Iron (Fe), % 73.3 to 77.5
0 to 0.25
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0.15 to 0.4
0
Nickel (Ni), % 0 to 0.3
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.15 to 0.4
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.080
Tin (Sn), % 0
0 to 0.2
Tungsten (W), % 17.3 to 19
0
Vanadium (V), % 0.75 to 1.3
0
Zinc (Zn), % 0
8.0 to 12
Residuals, % 0
0 to 0.7