SAE-AISI H42 Steel vs. EN 1.4864 Stainless Steel

Both SAE-AISI H42 steel and EN 1.4864 stainless steel are iron alloys. They have 51% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI H42 steel and the bottom bar is EN 1.4864 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 700 to 1980
650

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Melting Completion (Liquidus), °C 1620
1390
Melting Onset (Solidus), °C 1570
1340
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 24
13
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 24
30
Density, g/cm3 8.4
8.0
Embodied Carbon, kg CO2/kg material 8.8
5.3
Embodied Energy, MJ/kg 130
75
Embodied Water, L/kg 98
180

Common Calculations

PREN (Pitting Resistance) 31
17
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23 to 65
23
Strength to Weight: Bending, points 21 to 42
21
Thermal Diffusivity, mm2/s 6.5
3.3
Thermal Shock Resistance, points 20 to 57
17

Alloy Composition

Carbon (C), % 0.55 to 0.7
0 to 0.15
Chromium (Cr), % 3.8 to 4.5
15 to 17
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 79.3 to 83.8
41.7 to 51
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 4.5 to 5.5
0
Nickel (Ni), % 0 to 0.3
33 to 37
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 5.5 to 6.8
0
Vanadium (V), % 1.8 to 2.2
0