SAE-AISI L3 Steel vs. EN 1.4640 Stainless Steel
Both SAE-AISI L3 steel and EN 1.4640 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI L3 steel and the bottom bar is EN 1.4640 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 2250 | |
| 620 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1420 |
| Melting Onset (Solidus), °C | 1410 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 43 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.5 | |
| 14 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 27 | |
| 40 |
| Embodied Water, L/kg | 53 | |
| 150 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 80 | |
| 22 to 23 |
| Strength to Weight: Bending, points | 20 to 49 | |
| 21 |
| Thermal Diffusivity, mm2/s | 12 | |
| 4.0 |
| Thermal Shock Resistance, points | 18 to 67 | |
| 14 to 15 |
Alloy Composition
| Carbon (C), % | 1.0 to 1.1 | |
| 0.030 to 0.080 |
| Chromium (Cr), % | 1.3 to 1.7 | |
| 18 to 19 |
| Copper (Cu), % | 0 | |
| 1.3 to 2.0 |
| Iron (Fe), % | 95.5 to 97.3 | |
| 67.4 to 73.6 |
| Manganese (Mn), % | 0.25 to 0.8 | |
| 1.5 to 4.0 |
| Nickel (Ni), % | 0 | |
| 5.5 to 6.9 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.11 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.1 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |