SAE-AISI L3 Steel vs. EN 2.4879 Cast Nickel

SAE-AISI L3 steel belongs to the iron alloys classification, while EN 2.4879 cast nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI L3 steel and the bottom bar is EN 2.4879 cast nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
80
Tensile Strength: Ultimate (UTS), MPa 600 to 2250
490

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 43
11
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
55
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.9
8.3
Embodied Energy, MJ/kg 27
120
Embodied Water, L/kg 53
270

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21 to 80
16
Strength to Weight: Bending, points 20 to 49
16
Thermal Diffusivity, mm2/s 12
2.8
Thermal Shock Resistance, points 18 to 67
13

Alloy Composition

Carbon (C), % 1.0 to 1.1
0.35 to 0.55
Chromium (Cr), % 1.3 to 1.7
27 to 30
Iron (Fe), % 95.5 to 97.3
9.4 to 20.7
Manganese (Mn), % 0.25 to 0.8
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
47 to 50
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.1 to 0.5
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
4.0 to 6.0
Vanadium (V), % 0.1 to 0.3
0