SAE-AISI L6 Steel vs. EN 1.4877 Stainless Steel

Both SAE-AISI L6 steel and EN 1.4877 stainless steel are iron alloys. They have 43% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI L6 steel and the bottom bar is EN 1.4877 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
79
Tensile Strength: Ultimate (UTS), MPa 670 to 2090
630

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 42
12
Thermal Expansion, µm/m-K 11
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.6
37
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.0
6.2
Embodied Energy, MJ/kg 28
89
Embodied Water, L/kg 54
220

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 74
22
Strength to Weight: Bending, points 22 to 46
20
Thermal Diffusivity, mm2/s 11
3.2
Thermal Shock Resistance, points 22 to 70
15

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0.65 to 0.75
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 0.6 to 1.2
26 to 28
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.6 to 97.3
36.4 to 42.3
Manganese (Mn), % 0.25 to 0.8
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 1.3 to 2.0
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0 to 0.3
0