SAE-AISI M10 Steel vs. AISI 201L Stainless Steel

Both SAE-AISI M10 steel and AISI 201L stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M10 steel and the bottom bar is AISI 201L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 740 to 2170
740 to 1040

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Melting Completion (Liquidus), °C 1520
1410
Melting Onset (Solidus), °C 1470
1370
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 31
15
Thermal Expansion, µm/m-K 12
17

Otherwise Unclassified Properties

Base Metal Price, % relative 14
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 8.3
2.6
Embodied Energy, MJ/kg 120
38
Embodied Water, L/kg 100
140

Common Calculations

PREN (Pitting Resistance) 31
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26 to 76
27 to 37
Strength to Weight: Bending, points 23 to 47
24 to 30
Thermal Diffusivity, mm2/s 8.5
4.0
Thermal Shock Resistance, points 23 to 68
16 to 23

Alloy Composition

Carbon (C), % 0.84 to 1.1
0 to 0.030
Chromium (Cr), % 3.8 to 4.5
16 to 18
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 82.3 to 85.6
67.9 to 75
Manganese (Mn), % 0.1 to 0.4
5.5 to 7.5
Molybdenum (Mo), % 7.8 to 8.5
0
Nickel (Ni), % 0 to 0.3
3.5 to 5.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.2 to 0.45
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 1.8 to 2.2
0

Comparable Variants