SAE-AISI M10 Steel vs. ASTM A283 Carbon Steel
Both SAE-AISI M10 steel and ASTM A283 carbon steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M10 steel and the bottom bar is ASTM A283 carbon steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 76 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 740 to 2170 | |
360 to 480 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
250 |
Melting Completion (Liquidus), °C | 1520 | |
1460 |
Melting Onset (Solidus), °C | 1470 | |
1420 |
Specific Heat Capacity, J/kg-K | 460 | |
470 |
Thermal Conductivity, W/m-K | 31 | |
51 to 53 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 14 | |
1.8 |
Density, g/cm3 | 7.9 | |
7.8 to 7.9 |
Embodied Carbon, kg CO2/kg material | 8.3 | |
1.4 |
Embodied Energy, MJ/kg | 120 | |
18 |
Embodied Water, L/kg | 100 | |
46 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 26 to 76 | |
13 to 17 |
Strength to Weight: Bending, points | 23 to 47 | |
14 to 17 |
Thermal Diffusivity, mm2/s | 8.5 | |
14 |
Thermal Shock Resistance, points | 23 to 68 | |
11 to 15 |