SAE-AISI M10 Steel vs. EN 1.0452 Steel

Both SAE-AISI M10 steel and EN 1.0452 steel are iron alloys. They have 85% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M10 steel and the bottom bar is EN 1.0452 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 740 to 2170
430

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1520
1460
Melting Onset (Solidus), °C 1470
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 31
48
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 14
2.1
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 8.3
1.5
Embodied Energy, MJ/kg 120
19
Embodied Water, L/kg 100
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 76
15
Strength to Weight: Bending, points 23 to 47
16
Thermal Diffusivity, mm2/s 8.5
13
Thermal Shock Resistance, points 23 to 68
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0.84 to 1.1
0 to 0.17
Chromium (Cr), % 3.8 to 4.5
0 to 0.3
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 82.3 to 85.6
97.1 to 99.58
Manganese (Mn), % 0.1 to 0.4
0.4 to 1.2
Molybdenum (Mo), % 7.8 to 8.5
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.2 to 0.45
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 1.8 to 2.2
0 to 0.020