SAE-AISI M3 Class 2 Steel vs. ASTM Grade LC2 Steel

Both SAE-AISI M3 class 2 steel and ASTM grade LC2 steel are iron alloys. They have 80% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M3 class 2 steel and the bottom bar is ASTM grade LC2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 770 to 2210
570

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1620
1460
Melting Onset (Solidus), °C 1570
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 26
52
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.4
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 12
1.6
Embodied Energy, MJ/kg 180
22
Embodied Water, L/kg 110
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 26 to 74
20
Strength to Weight: Bending, points 22 to 45
19
Thermal Diffusivity, mm2/s 7.2
14
Thermal Shock Resistance, points 24 to 69
17

Alloy Composition

Carbon (C), % 1.2 to 1.3
0 to 0.25
Chromium (Cr), % 3.8 to 4.5
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 75.8 to 82.3
95.3 to 97.5
Manganese (Mn), % 0.15 to 0.4
0.5 to 0.8
Molybdenum (Mo), % 4.8 to 6.5
0
Nickel (Ni), % 0 to 0.3
2.0 to 3.0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.45
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.045
Tungsten (W), % 5.0 to 6.8
0
Vanadium (V), % 2.8 to 3.8
0