SAE-AISI M3 Class 2 Steel vs. EN 1.3555 Steel
Both SAE-AISI M3 class 2 steel and EN 1.3555 steel are iron alloys. They have 89% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M3 class 2 steel and the bottom bar is EN 1.3555 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 2210 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 260 |
| Melting Completion (Liquidus), °C | 1620 | |
| 1500 |
| Melting Onset (Solidus), °C | 1570 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 11 |
| Density, g/cm3 | 8.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 5.6 |
| Embodied Energy, MJ/kg | 180 | |
| 81 |
| Embodied Water, L/kg | 110 | |
| 90 |
Common Calculations
| PREN (Pitting Resistance) | 33 | |
| 18 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 74 | |
| 27 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 23 |
| Thermal Shock Resistance, points | 24 to 69 | |
| 22 |
Alloy Composition
| Carbon (C), % | 1.2 to 1.3 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.1 |
| Iron (Fe), % | 75.8 to 82.3 | |
| 85.4 to 87.7 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.35 |
| Molybdenum (Mo), % | 4.8 to 6.5 | |
| 4.0 to 4.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 3.2 to 3.6 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0.1 to 0.25 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Tungsten (W), % | 5.0 to 6.8 | |
| 0 to 0.15 |
| Vanadium (V), % | 2.8 to 3.8 | |
| 1.0 to 1.3 |