MakeItFrom.com
Menu (ESC)

SAE-AISI M33 Steel vs. EN 1.3567 Steel

Both SAE-AISI M33 steel and EN 1.3567 steel are iron alloys. They have 76% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M33 steel and the bottom bar is EN 1.3567 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 810 to 2210
500 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1550
1460
Melting Onset (Solidus), °C 1500
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 20
45
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 32
2.5
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 7.7
1.5
Embodied Energy, MJ/kg 110
20
Embodied Water, L/kg 150
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 75
18 to 50
Strength to Weight: Bending, points 24 to 46
18 to 36
Thermal Diffusivity, mm2/s 5.5
12
Thermal Shock Resistance, points 25 to 68
15 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.85 to 0.92
0.17 to 0.23
Chromium (Cr), % 3.5 to 4.0
0.9 to 1.2
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 71.4 to 76.3
96.8 to 98.4
Manganese (Mn), % 0.15 to 0.4
0.6 to 0.9
Molybdenum (Mo), % 9.0 to 10
0.15 to 0.25
Nickel (Ni), % 0 to 0.3
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.15 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 1.3 to 2.1
0
Vanadium (V), % 1.0 to 1.4
0

Comparable Variants