SAE-AISI M33 Steel vs. S35045 Stainless Steel

Both SAE-AISI M33 steel and S35045 stainless steel are iron alloys. They have 41% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M33 steel and the bottom bar is S35045 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 810 to 2210
540

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Melting Completion (Liquidus), °C 1550
1390
Melting Onset (Solidus), °C 1500
1340
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 20
12
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 32
34
Density, g/cm3 8.2
8.0
Embodied Carbon, kg CO2/kg material 7.7
5.8
Embodied Energy, MJ/kg 110
83
Embodied Water, L/kg 150
230

Common Calculations

PREN (Pitting Resistance) 38
27
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 75
19
Strength to Weight: Bending, points 24 to 46
19
Thermal Diffusivity, mm2/s 5.5
3.2
Thermal Shock Resistance, points 25 to 68
12

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0.85 to 0.92
0.060 to 0.1
Chromium (Cr), % 3.5 to 4.0
25 to 29
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0 to 0.75
Iron (Fe), % 71.4 to 76.3
29.4 to 42.6
Manganese (Mn), % 0.15 to 0.4
0 to 1.5
Molybdenum (Mo), % 9.0 to 10
0
Nickel (Ni), % 0 to 0.3
32 to 37
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.15 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6
Tungsten (W), % 1.3 to 2.1
0
Vanadium (V), % 1.0 to 1.4
0