SAE-AISI M36 Steel vs. EN 1.0033 Steel

Both SAE-AISI M36 steel and EN 1.0033 steel are iron alloys. They have 73% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M36 steel and the bottom bar is EN 1.0033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 810 to 2190
300 to 330

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1600
1470
Melting Onset (Solidus), °C 1550
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 19
53
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 38
1.8
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 9.5
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 140
45

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 27 to 72
10 to 12
Strength to Weight: Bending, points 23 to 44
13 to 14
Thermal Diffusivity, mm2/s 5.1
14
Thermal Shock Resistance, points 25 to 68
9.4 to 10

Alloy Composition

Carbon (C), % 0.8 to 0.9
0 to 0.11
Chromium (Cr), % 3.8 to 4.5
0
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 70.1 to 75.5
98.8 to 100
Manganese (Mn), % 0.15 to 0.4
0 to 0.7
Molybdenum (Mo), % 4.6 to 5.5
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.2 to 0.45
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045
Tungsten (W), % 5.5 to 6.5
0
Vanadium (V), % 1.8 to 2.3
0

Comparable Variants