SAE-AISI M36 Steel vs. Grade CW6MC Nickel
SAE-AISI M36 steel belongs to the iron alloys classification, while grade CW6MC nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M36 steel and the bottom bar is grade CW6MC nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 2190 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 330 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1480 |
| Melting Onset (Solidus), °C | 1550 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 440 |
| Thermal Conductivity, W/m-K | 19 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 80 |
| Density, g/cm3 | 8.4 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 9.5 | |
| 14 |
| Embodied Energy, MJ/kg | 140 | |
| 200 |
| Embodied Water, L/kg | 140 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 27 to 72 | |
| 18 |
| Strength to Weight: Bending, points | 23 to 44 | |
| 17 |
| Thermal Diffusivity, mm2/s | 5.1 | |
| 2.8 |
| Thermal Shock Resistance, points | 25 to 68 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.8 to 0.9 | |
| 0 to 0.060 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 20 to 23 |
| Cobalt (Co), % | 7.8 to 8.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 70.1 to 75.5 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 4.6 to 5.5 | |
| 8.0 to 10 |
| Nickel (Ni), % | 0 to 0.3 | |
| 55.4 to 68.9 |
| Niobium (Nb), % | 0 | |
| 3.2 to 4.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.015 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 5.5 to 6.5 | |
| 0 |
| Vanadium (V), % | 1.8 to 2.3 | |
| 0 |