SAE-AISI M36 Steel vs. SAE-AISI 1527 Steel

Both SAE-AISI M36 steel and SAE-AISI 1527 steel are iron alloys. They have 73% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M36 steel and the bottom bar is SAE-AISI 1527 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 810 to 2190
590 to 640

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1600
1460
Melting Onset (Solidus), °C 1550
1420
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 19
52
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 38
1.8
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.5
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 140
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 27 to 72
21 to 23
Strength to Weight: Bending, points 23 to 44
20 to 21
Thermal Diffusivity, mm2/s 5.1
14
Thermal Shock Resistance, points 25 to 68
19 to 20

Alloy Composition

Carbon (C), % 0.8 to 0.9
0.22 to 0.29
Chromium (Cr), % 3.8 to 4.5
0
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 70.1 to 75.5
98.1 to 98.6
Manganese (Mn), % 0.15 to 0.4
1.2 to 1.5
Molybdenum (Mo), % 4.6 to 5.5
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.2 to 0.45
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Tungsten (W), % 5.5 to 6.5
0
Vanadium (V), % 1.8 to 2.3
0