SAE-AISI M36 Steel vs. SAE-AISI T15 Steel
Both SAE-AISI M36 steel and SAE-AISI T15 steel are iron alloys. They have 90% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI M36 steel and the bottom bar is SAE-AISI T15 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 2190 | |
| 830 to 2240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1690 |
| Melting Onset (Solidus), °C | 1550 | |
| 1640 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 430 |
| Thermal Conductivity, W/m-K | 19 | |
| 21 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 43 |
| Density, g/cm3 | 8.4 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 9.5 | |
| 16 |
| Embodied Energy, MJ/kg | 140 | |
| 250 |
| Embodied Water, L/kg | 140 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 31 | |
| 27 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 22 |
| Strength to Weight: Axial, points | 27 to 72 | |
| 26 to 71 |
| Strength to Weight: Bending, points | 23 to 44 | |
| 22 to 43 |
| Thermal Diffusivity, mm2/s | 5.1 | |
| 5.6 |
| Thermal Shock Resistance, points | 25 to 68 | |
| 26 to 70 |
Alloy Composition
| Carbon (C), % | 0.8 to 0.9 | |
| 1.5 to 1.6 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 3.8 to 5.0 |
| Cobalt (Co), % | 7.8 to 8.8 | |
| 4.8 to 5.3 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 70.1 to 75.5 | |
| 67.5 to 73.5 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 4.6 to 5.5 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.45 | |
| 0.15 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 5.5 to 6.5 | |
| 11.8 to 13 |
| Vanadium (V), % | 1.8 to 2.3 | |
| 4.5 to 5.3 |