SAE-AISI M43 Steel vs. EN 2.4815 Cast Nickel
SAE-AISI M43 steel belongs to the iron alloys classification, while EN 2.4815 cast nickel belongs to the nickel alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M43 steel and the bottom bar is EN 2.4815 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 810 to 2290 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Melting Completion (Liquidus), °C | 1550 | |
| 1510 |
| Melting Onset (Solidus), °C | 1500 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 19 | |
| 25 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 47 |
| Density, g/cm3 | 8.2 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 7.9 |
| Embodied Energy, MJ/kg | 120 | |
| 110 |
| Embodied Water, L/kg | 140 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 27 to 77 | |
| 15 |
| Strength to Weight: Bending, points | 24 to 47 | |
| 16 |
| Thermal Diffusivity, mm2/s | 5.3 | |
| 6.4 |
| Thermal Shock Resistance, points | 25 to 71 | |
| 17 |
Alloy Composition
| Carbon (C), % | 1.2 to 1.3 | |
| 0.35 to 0.65 |
| Chromium (Cr), % | 3.5 to 4.3 | |
| 12 to 18 |
| Cobalt (Co), % | 7.8 to 8.8 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 70.8 to 76 | |
| 9.8 to 28.7 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 7.5 to 8.5 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 58 to 66 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.65 | |
| 1.0 to 2.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 2.3 to 3.0 | |
| 0 |
| Vanadium (V), % | 1.5 to 1.8 | |
| 0 |