SAE-AISI M44 Steel vs. N06650 Nickel

SAE-AISI M44 steel belongs to the iron alloys classification, while N06650 nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M44 steel and the bottom bar is N06650 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 78
82
Tensile Strength: Ultimate (UTS), MPa 870 to 2290
900

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1590
1500
Melting Onset (Solidus), °C 1540
1450
Specific Heat Capacity, J/kg-K 440
440
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 43
60
Density, g/cm3 8.4
8.6
Embodied Carbon, kg CO2/kg material 9.9
10
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 170
270

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 28 to 75
29
Strength to Weight: Bending, points 24 to 46
24
Thermal Shock Resistance, points 27 to 70
24

Alloy Composition

Aluminum (Al), % 0
0.050 to 0.5
Carbon (C), % 1.1 to 1.2
0 to 0.030
Chromium (Cr), % 4.0 to 4.8
19 to 21
Cobalt (Co), % 11 to 12.3
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 65.3 to 70.6
12 to 16
Manganese (Mn), % 0.2 to 0.4
0 to 0.5
Molybdenum (Mo), % 6.0 to 7.0
9.5 to 12.5
Nickel (Ni), % 0 to 0.3
44.4 to 58.9
Niobium (Nb), % 0
0.050 to 0.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.3 to 0.55
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Tungsten (W), % 5.0 to 5.8
0.5 to 2.5
Vanadium (V), % 1.9 to 2.2
0