SAE-AISI M44 Steel vs. R30816 Cobalt
SAE-AISI M44 steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI M44 steel and the bottom bar is R30816 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 78 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 870 to 2290 | |
| 1020 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 300 |
| Melting Completion (Liquidus), °C | 1590 | |
| 1540 |
| Melting Onset (Solidus), °C | 1540 | |
| 1460 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 420 |
| Thermal Conductivity, W/m-K | 14 | |
| 13 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 9.9 | |
| 20 |
| Embodied Energy, MJ/kg | 150 | |
| 320 |
| Embodied Water, L/kg | 170 | |
| 440 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 22 |
| Strength to Weight: Axial, points | 28 to 75 | |
| 31 |
| Strength to Weight: Bending, points | 24 to 46 | |
| 25 |
| Thermal Diffusivity, mm2/s | 3.7 | |
| 3.3 |
| Thermal Shock Resistance, points | 27 to 70 | |
| 28 |
Alloy Composition
| Carbon (C), % | 1.1 to 1.2 | |
| 0.32 to 0.42 |
| Chromium (Cr), % | 4.0 to 4.8 | |
| 19 to 21 |
| Cobalt (Co), % | 11 to 12.3 | |
| 40 to 49.8 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 65.3 to 70.6 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 6.0 to 7.0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 3.5 to 4.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.3 to 0.55 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 3.5 to 4.5 |
| Tungsten (W), % | 5.0 to 5.8 | |
| 3.5 to 4.5 |
| Vanadium (V), % | 1.9 to 2.2 | |
| 0 |