SAE-AISI M50 Steel vs. EN 1.4948 Stainless Steel

Both SAE-AISI M50 steel and EN 1.4948 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M50 steel and the bottom bar is EN 1.4948 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 720 to 2250
610

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1480
1430
Melting Onset (Solidus), °C 1440
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 35
17
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
15
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.1
3.0
Embodied Energy, MJ/kg 74
43
Embodied Water, L/kg 83
140

Common Calculations

PREN (Pitting Resistance) 19
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26 to 80
22
Strength to Weight: Bending, points 23 to 49
21
Thermal Diffusivity, mm2/s 9.7
4.5
Thermal Shock Resistance, points 21 to 66
14

Alloy Composition

Carbon (C), % 0.78 to 0.88
0.040 to 0.080
Chromium (Cr), % 3.8 to 4.5
17 to 19
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 87 to 90.4
66.8 to 75
Manganese (Mn), % 0.15 to 0.45
0 to 2.0
Molybdenum (Mo), % 3.9 to 4.8
0
Nickel (Ni), % 0 to 0.3
8.0 to 11
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.2 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0.8 to 1.3
0