SAE-AISI M50 Steel vs. SAE-AISI O7 Steel
Both SAE-AISI M50 steel and SAE-AISI O7 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common.
For each property being compared, the top bar is SAE-AISI M50 steel and the bottom bar is SAE-AISI O7 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 2250 | |
| 680 to 2110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1480 |
| Melting Onset (Solidus), °C | 1440 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 35 | |
| 41 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.7 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 6.0 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 2.3 |
| Embodied Energy, MJ/kg | 74 | |
| 33 |
| Embodied Water, L/kg | 83 | |
| 52 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 3.6 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 80 | |
| 24 to 74 |
| Strength to Weight: Bending, points | 23 to 49 | |
| 22 to 46 |
| Thermal Diffusivity, mm2/s | 9.7 | |
| 11 |
| Thermal Shock Resistance, points | 21 to 66 | |
| 23 to 70 |
Alloy Composition
| Carbon (C), % | 0.78 to 0.88 | |
| 1.1 to 1.3 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 0.35 to 0.85 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.25 |
| Iron (Fe), % | 87 to 90.4 | |
| 92.9 to 97.6 |
| Manganese (Mn), % | 0.15 to 0.45 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 3.9 to 4.8 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.2 to 0.6 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 1.0 to 2.0 |
| Vanadium (V), % | 0.8 to 1.3 | |
| 0 to 0.4 |