SAE-AISI M62 Steel vs. AISI 316 Stainless Steel

Both SAE-AISI M62 steel and AISI 316 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M62 steel and the bottom bar is AISI 316 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 830 to 2440
520 to 1180

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1650
1400
Melting Onset (Solidus), °C 1600
1380
Specific Heat Capacity, J/kg-K 430
470
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 30
19
Density, g/cm3 8.5
7.9
Embodied Carbon, kg CO2/kg material 10
3.9
Embodied Energy, MJ/kg 150
53
Embodied Water, L/kg 110
150

Common Calculations

PREN (Pitting Resistance) 49
26
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 27 to 80
18 to 41
Strength to Weight: Bending, points 23 to 47
18 to 31
Thermal Shock Resistance, points 24 to 71
11 to 26

Alloy Composition

Carbon (C), % 1.3 to 1.4
0 to 0.080
Chromium (Cr), % 3.5 to 4.0
16 to 18
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 73.6 to 77.4
62 to 72
Manganese (Mn), % 0.15 to 0.4
0 to 2.0
Molybdenum (Mo), % 10 to 11
2.0 to 3.0
Nickel (Ni), % 0 to 0.3
10 to 14
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.15 to 0.4
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 5.8 to 6.5
0
Vanadium (V), % 1.8 to 2.1
0