SAE-AISI M62 Steel vs. EN 1.1106 Steel

Both SAE-AISI M62 steel and EN 1.1106 steel are iron alloys. They have 77% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M62 steel and the bottom bar is EN 1.1106 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 830 to 2440
550

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1650
1460
Melting Onset (Solidus), °C 1600
1420
Specific Heat Capacity, J/kg-K 430
470
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.3
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.6
Embodied Energy, MJ/kg 150
22
Embodied Water, L/kg 110
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 27 to 80
19
Strength to Weight: Bending, points 23 to 47
19
Thermal Shock Resistance, points 24 to 71
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 1.3 to 1.4
0 to 0.18
Chromium (Cr), % 3.5 to 4.0
0 to 0.3
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 73.6 to 77.4
96.2 to 98.9
Manganese (Mn), % 0.15 to 0.4
1.1 to 1.7
Molybdenum (Mo), % 10 to 11
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.15 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Tungsten (W), % 5.8 to 6.5
0
Vanadium (V), % 1.8 to 2.1
0 to 0.1