SAE-AISI M62 Steel vs. C95700 Bronze

SAE-AISI M62 steel belongs to the iron alloys classification, while C95700 bronze belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M62 steel and the bottom bar is C95700 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
130
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 79
47
Tensile Strength: Ultimate (UTS), MPa 830 to 2440
680

Thermal Properties

Latent Heat of Fusion, J/g 260
230
Melting Completion (Liquidus), °C 1650
990
Melting Onset (Solidus), °C 1600
950
Specific Heat Capacity, J/kg-K 430
440
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 30
26
Density, g/cm3 8.5
8.2
Embodied Carbon, kg CO2/kg material 10
3.3
Embodied Energy, MJ/kg 150
54
Embodied Water, L/kg 110
360

Common Calculations

Stiffness to Weight: Axial, points 13
8.5
Stiffness to Weight: Bending, points 23
20
Strength to Weight: Axial, points 27 to 80
23
Strength to Weight: Bending, points 23 to 47
21
Thermal Shock Resistance, points 24 to 71
21

Alloy Composition

Aluminum (Al), % 0
7.0 to 8.5
Carbon (C), % 1.3 to 1.4
0
Chromium (Cr), % 3.5 to 4.0
0
Copper (Cu), % 0 to 0.25
71 to 78.5
Iron (Fe), % 73.6 to 77.4
2.0 to 4.0
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0.15 to 0.4
11 to 14
Molybdenum (Mo), % 10 to 11
0
Nickel (Ni), % 0 to 0.3
1.5 to 3.0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.15 to 0.4
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 5.8 to 6.5
0
Vanadium (V), % 1.8 to 2.1
0
Residuals, % 0
0 to 0.5