SAE-AISI O2 Steel vs. Austempered Cast Iron
Both SAE-AISI O2 steel and austempered cast iron are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI O2 steel and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 62 to 69 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 2050 | |
| 860 to 1800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1380 |
| Melting Onset (Solidus), °C | 1410 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 490 |
| Thermal Conductivity, W/m-K | 43 | |
| 42 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 2.9 |
| Density, g/cm3 | 7.8 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.8 |
| Embodied Energy, MJ/kg | 26 | |
| 25 |
| Embodied Water, L/kg | 50 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 73 | |
| 32 to 66 |
| Strength to Weight: Bending, points | 21 to 46 | |
| 27 to 44 |
| Thermal Diffusivity, mm2/s | 12 | |
| 11 |
| Thermal Shock Resistance, points | 22 to 70 | |
| 25 to 53 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Arsenic (As), % | 0 | |
| 0 to 0.020 |
| Carbon (C), % | 0.85 to 1.0 | |
| 3.4 to 3.8 |
| Chromium (Cr), % | 0 to 0.5 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.8 |
| Iron (Fe), % | 95 to 97.8 | |
| 89.6 to 94 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.040 |
| Manganese (Mn), % | 1.4 to 1.8 | |
| 0.3 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 2.3 to 2.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Tin (Sn), % | 0 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 to 0.3 | |
| 0 to 0.1 |