SAE-AISI O2 Steel vs. Grade 200 Maraging Steel
Both SAE-AISI O2 steel and grade 200 maraging steel are iron alloys. They have 70% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI O2 steel and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 72 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 2050 | |
| 970 to 1500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 31 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 4.5 |
| Embodied Energy, MJ/kg | 26 | |
| 59 |
| Embodied Water, L/kg | 50 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 23 to 73 | |
| 33 to 51 |
| Strength to Weight: Bending, points | 21 to 46 | |
| 27 to 35 |
| Thermal Shock Resistance, points | 22 to 70 | |
| 29 to 45 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.85 to 1.0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.5 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 8.0 to 9.0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 95 to 97.8 | |
| 67.8 to 71.8 |
| Manganese (Mn), % | 1.4 to 1.8 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 17 to 19 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.25 |
| Vanadium (V), % | 0 to 0.3 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |