SAE-AISI O6 Steel vs. EN 1.4710 Stainless Steel

Both SAE-AISI O6 steel and EN 1.4710 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI O6 steel and the bottom bar is EN 1.4710 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 71
74

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 43
24
Thermal Expansion, µm/m-K 12
9.9

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
6.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
7.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
5.0
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 21
24
Embodied Water, L/kg 47
76

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Thermal Diffusivity, mm2/s 12
6.5

Alloy Composition

Carbon (C), % 1.3 to 1.6
0.2 to 0.35
Chromium (Cr), % 0 to 0.3
6.0 to 8.0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 94.6 to 97.7
87.4 to 92.3
Manganese (Mn), % 0.3 to 1.1
0.5 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0 to 0.15
Nickel (Ni), % 0 to 0.3
0 to 0.5
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.55 to 1.5
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030