MakeItFrom.com
Menu (ESC)

SAE-AISI O6 Steel vs. SAE-AISI M52 Steel

Both SAE-AISI O6 steel and SAE-AISI M52 steel are iron alloys. They have 89% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI O6 steel and the bottom bar is SAE-AISI M52 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 71
75
Tensile Strength: Ultimate (UTS), MPa 670 to 2070
710 to 2280

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Melting Completion (Liquidus), °C 1430
1510
Melting Onset (Solidus), °C 1390
1470
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 43
31
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
10

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
12
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 1.5
7.5
Embodied Energy, MJ/kg 21
110
Embodied Water, L/kg 47
89

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 74
25 to 80
Strength to Weight: Bending, points 22 to 47
22 to 49
Thermal Diffusivity, mm2/s 12
8.4
Thermal Shock Resistance, points 22 to 69
21 to 67

Alloy Composition

Carbon (C), % 1.3 to 1.6
0.85 to 1.0
Chromium (Cr), % 0 to 0.3
3.5 to 4.3
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 94.6 to 97.7
84.4 to 88.9
Manganese (Mn), % 0.3 to 1.1
0.15 to 0.45
Molybdenum (Mo), % 0.2 to 0.3
4.0 to 4.9
Nickel (Ni), % 0 to 0.3
0 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.55 to 1.5
0.2 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
0.75 to 1.5
Vanadium (V), % 0
1.7 to 2.3

Comparable Variants