SAE-AISI O7 Steel vs. EN 1.3537 Steel

Both SAE-AISI O7 steel and EN 1.3537 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI O7 steel and the bottom bar is EN 1.3537 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 680 to 2110
620 to 730

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1480
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
43
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.0
2.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.5
Embodied Energy, MJ/kg 33
21
Embodied Water, L/kg 52
54

Common Calculations

PREN (Pitting Resistance) 3.6
2.6
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24 to 74
22 to 26
Strength to Weight: Bending, points 22 to 46
21 to 23
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 23 to 70
18 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 1.1 to 1.3
0.93 to 1.1
Chromium (Cr), % 0.35 to 0.85
1.7 to 2.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 92.9 to 97.6
96.4 to 97.8
Manganese (Mn), % 0 to 1.0
0.25 to 0.45
Molybdenum (Mo), % 0 to 0.3
0.15 to 0.3
Nickel (Ni), % 0 to 0.3
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.6
0.15 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 1.0 to 2.0
0
Vanadium (V), % 0 to 0.4
0