SAE-AISI O7 Steel vs. EN 2.4879 Cast Nickel
SAE-AISI O7 steel belongs to the iron alloys classification, while EN 2.4879 cast nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI O7 steel and the bottom bar is EN 2.4879 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 2110 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1450 |
| Melting Onset (Solidus), °C | 1430 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 41 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.0 | |
| 55 |
| Density, g/cm3 | 7.9 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 33 | |
| 120 |
| Embodied Water, L/kg | 52 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 74 | |
| 16 |
| Strength to Weight: Bending, points | 22 to 46 | |
| 16 |
| Thermal Diffusivity, mm2/s | 11 | |
| 2.8 |
| Thermal Shock Resistance, points | 23 to 70 | |
| 13 |
Alloy Composition
| Carbon (C), % | 1.1 to 1.3 | |
| 0.35 to 0.55 |
| Chromium (Cr), % | 0.35 to 0.85 | |
| 27 to 30 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 92.9 to 97.6 | |
| 9.4 to 20.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 47 to 50 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.6 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 1.0 to 2.0 | |
| 4.0 to 6.0 |
| Vanadium (V), % | 0 to 0.4 | |
| 0 |