SAE-AISI P20 Steel vs. S40910 Stainless Steel
Both SAE-AISI P20 steel and S40910 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI P20 steel and the bottom bar is S40910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 1050 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 45 | |
| 26 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.0 |
| Embodied Energy, MJ/kg | 21 | |
| 28 |
| Embodied Water, L/kg | 52 | |
| 94 |
Common Calculations
| PREN (Pitting Resistance) | 2.6 | |
| 11 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 37 | |
| 16 |
| Strength to Weight: Bending, points | 19 to 29 | |
| 16 |
| Thermal Diffusivity, mm2/s | 12 | |
| 6.9 |
| Thermal Shock Resistance, points | 18 to 35 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.28 to 0.4 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0.4 to 2.0 | |
| 10.5 to 11.7 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 95.2 to 98.5 | |
| 85 to 89.5 |
| Manganese (Mn), % | 0.35 to 0.71 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.3 to 0.55 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.17 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.5 |